Resins for Coatings from China — Manufacturer | Ningbo MOS Chemical Co., Ltd.

Acrylic Resins

Product Name	Brand	Tg (°C)	Mw	Viscosity (mPa·s)	Acid Value (mg KOH)	Solubility	Features	Applications
A-01	MOSINTER	59	75000	250-500 45.5% in ethyl acetate	28	Ar,K,E,P,G*	Good pigment dispersion; General purpose Good Adhesion and Flexibility High price-to-quality ratio	Industrial coatings; Road marking paint Anticorrosion coatings
A-01B	MOSINTER	59	90000	240-400 39.5% in ethyl acetate	4.5	Ar,K,E,P,G*	Good water and alcohol resistance Good Adhesion and Flexibility General purpose; High cost/performance ratio	Industrial coatings; Anticorrosive coatings Solvent-based container paint
A-01C	MOSINTER	59	75000	250-500 45.5% in ethyl acetate	28	Ar,K,E,P,G*	Low VOC content High price-to-quality ratio Good Adhesion and Flexibility	UV coatings; UV primer
A-02	MOSINTER	55	75000	250-550 45.5% in ethyl acetate	28	Ar,K,E,P,G*	Good water and alcohol resistance General Purpose High price-to-quality ratio	Road marking paint; Floor coatings
A-04	MOSINTER	78	70000	250-500 37% in ethyl acetate	5	Ar,K,E,P,G	Excellent weather resistance Excellent resistance to alcohols and salt spray Good adhesion to PET	Anticorrosion coatings Floor Coatings; PET Inks
A-05	MOSINTER	85	60000	250-500 40% in ethyl acetate	4	Ar,K,E,P,G	High hardness Fast drying	Industrial coatings
A-06	MOSINTER	50	40000	100-300 43.5% in ethyl acetate	18	Ar,K,E,P,G	Good wetting and dispersion	Industrial anti-corrosion coatings
A-10	MOSINTER	45	200000	180-400 30% in Solvent Naphtha/Butyl Alcohol 85/15	5	Ar,K,E,P,PA,G*	Good flexibility, dispersing Excellent weather resistance Soluble in Solvent Naphtha 200#	Fire Protective Coatings; Adhesives High-performance coatings for exterior use
A-10A	MOSINTER	45	200000	180-400 30% in Solvent Naphtha/Butyl Alcohol 85/15	5	Ar,K,E,P,PA,G*	Low VOC content Residual benzene free Good Weather Resistance	Eco-friendly adhesives and inks for tobacco packaging
A-13	MOSINTER	80	85000	1800-4000 36% in Ethyl Acetate	4	Ar,K,E,G*	Excellent protection against chemicals, alcohols, and scratches; High gloss	Plastic paint
A-17	MOSINTER	56	40000	1800-4500 51% in ethyl acetate	4	Ar,K,E,P,G	Good Flow and Leveling Good solubility and dispersion	Paint for plastics; Industrial coatings Leather Polish
A-24B	MOSINTER	34	150000	300-500 40% in MEK	3	Ar,K,E,P,G	Excellent adhesion and flexibility	Thermal Transfer Printing Aquaprint (hydrographic printing) Ceramic Decals; Adhesives
A-200	MOSINTER	63	50000	100-300 39.5% in ethyl acetate	7	Ar,K,E,G*	Good compatibility with CAB Good wetting and dispersion Optimized balance between flexibility and rigidity	Container paint; Road marking paint Industrial anti-corrosion coatings Inks and Adhesives

*This product can be dissolved in one or more solvents from this category.
A: alcohols, Ar: aromatic hydrocarbons, P: petroleum ether, E: esters, G: glycol ethers, K: ketones, PA: pure aliphatic hydrocarbons

Product Name	Brand	Tg (°C)	Mw	Viscosity (mPa·s)	Acid Value (mg KOH)	Hydroxyl Value (mgKOH)	Solubility	Features	Applications
A-50	MOSINTER	50	55000	200-500 39.5% in ethyl acetate	4		Ar,K,E,G*	Excellent wetting and dispersion Good compatibility with CAB	Thermal transfer inks; Adhesives
A-53A	MOSINTER	30	30000	180-400 30% in Solvent Naphtha	2	20	Ar,K,E,P*,PA,A	Soluble in alcohol; Excellent adhesion Compatible with alkyd resin group Excellent wetting and dispersion
A-54B	MOSINTER	55	55000	400-650 40% in xylene	6		Ar,K,E,G*	Excellent wetting and dispersion Good compatibility with CAB	Thermal transfer inks; Adhesives
A-58	MOSINTER	52	70000	2000-3000 50% in xylene	4		Ar,K,E,P,G	Good pigment dispersion High transparency	Floor paint; Industrial paint Woodworking
A-66	MOSINTER	50	48000	1800-4500 51% in ethyl acetate	4		Ar,K,E,P,G	Good compatibility with CAB	Topcoat; Industrial paint and inks
A-76	MOSINTER	76	35000	150-400 38.5% in ethyl acetate	4		Ar,K,E,G*	Good wetting and dispersion Good solvent resistance Low Odor	Thermal transfer release coatings UV coatings.
A-725	MOSINTER	61	45000	250-500 39.5% in ethyl acetate	6		Ar,K,E,P,G*		Industrial Coatings; PVC Inks.
A-728	MOSINTER	110	90000	350-600 30% in MEK	6		Ar,K,E,G*	High hardness Good Resistance to Alcohols and Solvents	Industrial inks; Varnishes Thermal Transfer Printing
A-811	MOSINTER	105	50000	40-180 25% in Ethyl Acetate	5		Ar,K,E,G*	High hardness Good Resistance to Alcohols and Solvents	Industrial inks; Varnishes Thermal Transfer Printing
A-15	MOSINTER	50	120000	500-1000 40% in MEK	5		Ar,K,E,G*	Excellent flexibility and solvent resistance
A-2210	MOSINTER	68	60000	450-600 40% in xylene	0		Ar,K,E,G*	Excellent flexibility and weather resistance Low acid value	Inks and Adhesives
A-2219	MOSINTER	75	30000	80-250 38.5% in ethyl acetate	5	6	Ar,K,E,G*	Low VOC content High hardness Good dispersion	Inks and Adhesives
A-2230	MOSINTER	76	40000	200-400 38.5% in ethyl acetate	11		Ar,K,E,G*	Good dispersing and adhesion High initial bond strength for adhesives

*This product can be dissolved in one or more solvents from this category.
A: alcohols, Ar: aromatic hydrocarbons, P: petroleum ether, E: esters, G: glycol ethers, K: ketones, PA: pure aliphatic hydrocarbons

Highly weather-resistant hydroxyl-containing acrylic resins

Product Name	Brand	Features	Applications
Synocure® 927 9S 70	ARKEMA	Hydroxyl content (on solids) 4.2, solid content 70%, Solvent: Butyl Acetate / Xylene, viscosity 6500 – 8500 mPa·s	Fast drying, good initial hardness, and outdoor weather resistance
Synocure® 854 BA 80	ARKEMA	Hydroxyl content (on solids) 2.1, solid content 80%, Solvent: Butyl acetate, viscosity 6900 - 9000 mPa·s	Low NCO demand, suitable for economical anticorrosive and marine coatings meeting VOC standards

Bio-Based Products

Product Name	Brand	Features	Applications
H1000 / H2000	AZELIS	100% bio-based, a polyester obtained by direct polymerization of PDO fermented from industrial corn; compared to petroleum-based polyesters, it offers higher low-temperature elasticity and hydrophilicity	Mainly used in PU/synthetic leather/chemical fibers/elastomers, personal care products, and other fields.

Silicone Resins

Product Name	Brand	Viscosity at room temperature [mPa·s]	Solid Content (%)	Features	Applications
TSR116	MOMENTIVE	150	50	Good impact strength	Heat-resistant coatings, anti-corrosion coatings, fiberglass impregnation, metallic magnetic powders
TSR117	MOMENTIVE	150	50	High hardness	Heat-resistant coatings, anti-corrosion coatings, fiberglass impregnation, metallic magnetic powders
TSR144	MOMENTIVE	100	50	Room-temperature curing	Heat-resistant coatings, anti-corrosion coatings, fiberglass impregnation, metallic magnetic powders
TSR1452 TSR145 TSR1452C	MOMENTIVE	40	60	High-Temperature Color and Gloss Retention	Heat-resistant coatings, anti-corrosion coatings, fiberglass impregnation, metallic magnetic powders
TSR165	MOMENTIVE	80	100	Low Molecular Weight	Silicone intermediate for modifying industrial anticorrosive coatings
YR3370	MOMENTIVE	Solid	100	Low smoke generation	Electrical insulation, heat-resistant coatings, powder coatings
TSR194	MOMENTIVE	180	50	High Hardness, 2H, Epoxy Modification	Heat-resistant coatings, industrial anti-corrosion coatings, metallic magnetic powders.
P905	MOMENTIVE	30000	50	High heat resistance, excellent adhesion and anticorrosive properties	Water-based silicone resin emulsion, heat-resistant coatings

Liquid BPA epoxy resins

Product Name	Brand	Epoxy Equivalent (g/eq)	Viscosity (cps, @ 25 °C)	Features and Applications
NPEL-127(E)	NAN YA	176 - 184	8,000 - 11,000	Standard low-viscosity resin; E series suitable for electronic-grade products
NPEL-128(E)	NAN YA	184 - 190	12,000 - 15,000	Standard general-purpose resin, E series suitable for electronic-grade products
NPEL-128R	NAN YA	184 - 194	12,000 - 16,000	Low-crystallizing resin, suitable for civil engineering, coatings

Solvent-Based Epoxy Resins

Product Name	Brand	Epoxy Equivalent (g/eq)	Viscosity (cps, @ 25 °C)	Features and Applications
NPSN-134X80	NAN YA	230 - 270	800 - 1,400	Bisphenol A epoxy resin, offering good strength, flexibility, and adhesion, etc.
NPSN-301X75	NAN YA	450 - 500	6,000 - 14,000	Good salt spray resistance, used in marine engineering
NPSN-901X75	NAN YA	450 - 500	8,000 - 15,000	Excellent flexibility and impact resistance, widely used for anti-corrosion protection of steel structures
NPSN-608BM50	NAN YA	2,000 - 2,500	3,000 - 6,500	High molecular weight epoxy resin with high flow, containing BSC/XYL solvent
NPEU-153K75	NAN YA	280.0 - 305.0	500 - 2,500	Bisphenol A epoxy resin modified with isocyanate, featuring high crosslink density, strong adhesion, and heat resistance.

Solid BPA epoxy resins

Product Name	Brand	Epoxy Equivalent (g/eq)	Viscosity (cps, @ 25 °C)	Features and Applications
NPES-301	NAN YA	450 - 500	60 - 70	Low molecular weight, direct-method production, base resin
NPES-302	NAN YA	600 - 700	75 - 85	Powder for electrical insulation, direct method production
NPES-303L	NAN YA	720 - 760	85 - 95	Direct process manufacturing
NPES-901	NAN YA	450 - 500	64 - 74	For lamination, excellent water resistance, chemical resistance, good impact resistance and flow
NPES-902	NAN YA	600 - 650	82 - 92	For Powder Coatings
NPES-903	NAN YA	700 - 750	90 - 98	For Powder Coatings
NPES-903H	NAN YA	740 - 800	92 - 100	For Powder Coatings
NPES-904	NAN YA	780 - 850	96 - 107	For Powder Coatings
NPES-904H	NAN YA	840 - 900	100 - 112	For Powder Coatings
NPES-907	NAN YA	1,500 - 1,800	120 - 130	For can coatings and hot-varnish applications
NPES-909	NAN YA	1,800 - 2,500	130 - 150	For can coatings and baking varnishes, excellent flexibility and storage stability

Industrial water-based emulsions

Product Name	Brand	Composition	Tg (°C)	MTPP (°C)	Solid content	pH	Features
PLIOTEC™ HDT 16	SYNTHOMER	Modified Acrylic Acid	28	20	50%	8.0	Industrial protective anticorrosive coatings and primers, direct-to-metal (DTM) application, low volatile organic compound (VOC) content
PLIOTEC™ HDT 12	SYNTHOMER	Modified Acrylic Acid	52	52	50%	8.5	Industrial protective anticorrosive coatings and primers, direct-to-metal (DMT) application, fast curing
LIPATON™ SB 5521	SYNTHOMER	Modified Styrene-Butadiene	-5	0	50%	8.5	Used for anticorrosive primers of passenger cars, trucks, ACE, and automotive underbody coatings.
REVACRYL™ AE 6030	SYNTHOMER	Modified Acrylic Acid	38	32	50%	8.0	Industrial protective anticorrosive primers
PLEXTOL™ R 5530	SYNTHOMER	Modified Acrylic Acid	28	23	47%	8.5	Anti-corrosion and direct-to-metal application, strong salt spray resistance
PLIOTEC™ SD 100	SYNTHOMER	Modified Acrylic Acid	13	0	62%	6.0	Used for water-based damping coatings (LASD) in the automotive or transportation industry

Intumescent Fire Protective Coatings (Solvent-based)

Product Name	Brand	Composition	Tg (°C)	Solubility (KB value)	Rheology	System	Features
PLIOLITE™ AC90	SYNTHOMER	Modified Acrylic Acid	54	40	Newtonian fluid	Solvent-Based	Multifunctional resin for solvent-based intumescent coatings, fire resistance R30-120 minutes; excellent water resistance and adhesion, outdoor durability reaches class X.
PLIOLITE™ AC80	SYNTHOMER	Modified Acrylic Acid	53	40	Newtonian fluid	Solvent-Based	Multifunctional resin for solvent-based intumescent coatings, fire resistance R30-120 minutes; excellent water resistance and adhesion, outdoor durability reaches class X.
PLIOLITE™ AC4	SYNTHOMER	Styrene-acrylic acid copolymer	54	45	Newtonian fluid	Solvent-Based	Film is strong and wear-resistant, good durability, excellent adhesion and weather resistance, viscosity adjustment, best used in combination with AC80
PLIOLITE™ VTAC-L	SYNTHOMER	Vinyltoluene Acrylic Acid	58	36	Newtonian fluid	Solvent-Based	Multifunctional resin for solvent-based intumescent coatings, fire resistance R90-120 minutes, provides rigid foam; excellent water resistance and adhesion, outdoor durability reaches class X
PLIOWAY™ EC1	SYNTHOMER	Substituted modified acrylic acid	56	31	Newtonian fluid	Solvent-Based	Multifunctional resin for solvent-based intumescent coatings, fire resistance R30-60 minutes, rapid carbonization; excellent water resistance and adhesion, outdoor durability reaches class X

Intumescent Fire Protective Coatings (Water-based)

Product Name	Brand	Composition	Tg (°C)	MTPP (°C)	Solid content	pH	System	Features
EMULTEX™ FR 728	SYNTHOMER	VA Copolymer	23	13	50%	4.0	Waterborne	Used for formulating water-based intumescent fireproof coatings, fire resistance R30-60 minutes, high expansion ratio, suitable for protecting steel and wood.
EMULTEX™ FR 797	SYNTHOMER	VA Copolymer	13	2	55%	4.5	Waterborne	Used for formulating water-based intumescent fireproof coatings, fire resistance R90-120 minutes, low expansion ratio, suitable for protecting steel and wood.

Vinyl chloride copolymers (Chlorinated vinyl resins)

Product Name	Brand	Vinyl chloride [wt%¹]	Other monomers [wt%¹]	Hydroxyl group content [wt%¹]	Glass transition temperature Tg (DSC) °C⁴	K-value²	Viscosity⁵ DIN 53015 [mPa·s]	Applications
No functional groups
VINNOL® E 15/45	WACKER	85.0 ± 1.0	-	-	Approx. 75	45 ± 1	37 ± 5	Coatings for leather, color chips, color pastes, various printing inks
VINNOL® E 18/38	WACKER	82.0 ± 1.0	-	-	Approx. 70	38 ± 1	15 ± 4	Inkjet printing inks
VINNOL® H 14/36	WACKER	85.6 ± 1.0	-	-	Approx. 69	35 ± 1	13 ± 3	Removable coatings, stone coatings, gravure printing, inkjet inks
VINNOL® H 15/42	WACKER	86.0 ± 1.0	-	-	Approx. 70	42 ± 1	28 ± 5	Removable coatings, stone coatings, gravure printing, inkjet inks, color chips, color pastes
VINNOL® H 15/50	WACKER	85.0 ± 1.0	-	-	Approx. 74	50 ± 1	70 ± 10	Adhesives, leather paints, strippable coatings, heat-seal coatings, color chips, screen printing inks
VINNOL® H 11/59	WACKER	89.0 ± 1.0	-	-	Approx. 75	59 ± 1	450 ± 100	Adhesives, Removable Coatings, Screen Printing Inks
VINNOL® P 15 C	WACKER	85.0 ± 1.0	-	-	Approx. 74	50 ± 1	70	Color chips, color pastes, heat-seal lacquers, printing inks, strippable lacquers, binders
VINNOL® H 40/43	WACKER	65.7 ± 1.0	-	-	Approx. 26	42 ± 1	25 ± 5	Removable coatings, transparent wood varnishes, stone coatings, heat-seal coatings, thermal transfer inks, gravure printing.
VINNOL® H 40/50	WACKER	63.0 ± 1.0	-	-	Approx. 45	50 ± 1	55 ± 10	Adhesives, leather paints, peelable coatings, heat-seal coatings, thermal transfer paints
VINNOL® H 40/60	WACKER	61.0 ± 1.0	-	-	About 145	60 ± 1	180 ± 30	Adhesives, leather coatings, strippable coatings, heat-seal coatings, thermal transfer inks, screen printing inks
VINNOL® P 38 C	WACKER	61.0 ± 1.0	-	-	Approx. 62	60 ± 1	180 ± 30	Leather coatings, adhesives, strippable coatings, paper and film coatings
With carboxyl groups
VINNOL® E 15/45 M	WACKER	84.0 ± 1.0	About 1.0	-	Approx. 73	45 ± 1	40 ± 5	Primers for metal and plastic, heat-seal coatings, protective coatings for aluminized films, printing inks
VINNOL® H 15/45 M	WACKER	84.0 ± 1.0	About 1.0	-	Approx. 74	48 ± 1	60 ± 10	Primers for metal and plastic, heat-sealable coatings, protective coatings for aluminized films, screen printing, heat transfer inks, adhesives
VINNOL® H 30/48 M	WACKER	70.0 ± 1.0	About 1.0	-	Approx. 65	48 ± 1	45 ± 10	Primers for metal and plastic, heat-sealable coatings, protective coatings for aluminized films, screen printing, thermal transfer inks
With hydroxyl groups
VINNOL® E 15/40 A	WACKER	84.0 ± 1.0	Approx. 16.0⁶	1.8 ± 0.2	Approx. 69	39 ± 1	20 ± 5	Primers for metal and plastic, heat-sealable coatings, wood varnishes, gravure printing, inkjet inks, adhesives, color chips
VINNOL® E 15/48 A	WACKER	83.5 ± 1.0	Approx. 16.5⁶	1.8 ± 0.2	Approx. 69	48 ± 1	60 ± 10	Synthetic leather, clear wood varnishes, gravure printing, screen printing inks, adhesives, color chips
VINNOL® E 22/48 A	WACKER	75.0 ± 1.0	Approx. 25.0⁶/⁷	1.8 ± 0.2	Approx. 61	48 ± 1	45 ± 7	Heat-resistant sealing coatings, stoving lacquers, clear wood varnishes, gravure printing, color chips

* Note:
¹ Test method Wacker; ² EN ISO 1628-2; ⁴ The above data are intended as usage guidance and should not be used for product specification purposes;
⁵ 20% solution (Solvent: methyl ethyl ketone), dissolution temperature 50°C; ⁶ Hydroxypropyl acrylate; ⁷ Vinyl acetate;

Resins and Binders for Coatings from a Chinese Manufacturer

Chinese manufacturer of coatings raw materials

International Brands in Distribution

Formulation selection

Wholesale and global supply

Catalog resins and binders for coatings