Polymers and binders Synthomer
Total 13 productsThe page presents 13 Synthomer products, including the PLIOTEC™, LIPATON™, REVACRYL™, PLEXTOL™, PLIOLITE™, PLIOWAY™, and EMULTEX™ series. The materials are used in waterborne industrial coatings, anticorrosive primers, direct-to-metal systems, automotive and anti-vibration coatings, and intumescent fire-retardant systems. Ningbo MOS Chemical Co., Ltd. provides grade selection, packaging confirmation, available documentation, and wholesale supply to B2B clients worldwide.
Synthomer — aqueous industrial emulsions
| Name | Composition | Tg (°C) | Minimum film-forming temperature (°C) | Solids content | pH | Features |
|---|---|---|---|---|---|---|
| PLIOTEC™ HDT 16 | Modified acrylate | 28 | 20 | 50% | 8.0 | Industrial protective anti-corrosion coatings and primers, direct-to-metal (DTM) application, low VOC |
| PLIOTEC™ HDT 12 | Modified acrylate | 52 | 52 | 50% | 8.5 | Industrial protective anticorrosive coatings and primers, direct-to-metal (DTM) application, fast curing |
| LIPATON™ SB 5521 | Modified Styrene-Butadiene | -5 | 0 | 50% | 8.5 | Industrial anticorrosive primers and coatings for automotive underbody, trucks, and ACE |
| REVACRYL™ AE 6030 | Modified Acrylic Acid | 38 | 32 | 50% | 8.0 | Industrial protective anticorrosive primers |
| PLEXTOL™ R 5530 | Modified acrylate | 28 | 23 | 47% | 8.5 | Anti-corrosion coating with direct-to-metal application; high salt spray resistance |
| PLIOTEC™ SD 100 | Modified acrylate | 13 | 0 | 62% | 6.0 | Water-based anti-vibration coatings (LASD) for the automotive and transportation industry |
Synthomer — intumescent fire protective coatings on solvents
| Name | Composition | Tg (°C) | Solubility (KB) | Rheology | System | Features |
|---|---|---|---|---|---|---|
| PLIOLITE™ AC90 | Modified Acrylic Acid | 54 | 40 | Newtonian fluid | Solvent-Based | Multifunctional resin for solvent-based intumescent coatings; fire resistance R30-120 min; good water resistance and adhesion; weatherability class X. |
| PLIOLITE™ AC80 | Modified Acrylic Acid | 53 | 40 | Newtonian fluid | Solvent-Based | Multifunctional resin for solvent-based intumescent coatings; fire resistance R30-120 min; good water resistance and adhesion; weatherability class X. |
| PLIOLITE™ AC4 | Styrene-acrylic acid copolymer | 54 | 45 | Newtonian fluid | Solvent-Based | Hard and wear-resistant film; good durability; excellent adhesion and weather resistance; adjustable viscosity; recommended for use with AC80 |
| PLIOLITE™ VTAC-L | Ethylene Acrylate | 58 | 36 | Newtonian fluid | Solvent-Based | Multifunctional resin for solvent-based intumescent coatings; fire resistance R90-120 min; rigid foam; good water resistance and adhesion; weatherability class X. |
| PLIOWAY™ EC1 | Alternative modified acrylic acid | 56 | 31 | Newtonian fluid | Solvent-Based | Multifunctional resin for solvent-based intumescent coatings; fire resistance R30-60 min; fast curing; good water resistance and adhesion; weatherability class X. |
Synthomer — waterborne intumescent fire protective coatings
| Name | Composition | Tg (°C) | Minimum film-forming temperature (°C) | Solids content | pH | System | Features |
|---|---|---|---|---|---|---|---|
| EMULTEX™ FR 728 | VA Copolymer | 23 | 13 | 50% | 4.0 | Water-based | Waterborne intumescent fire protective coatings; fire resistance R30-60 min; high expansion ratio; protection for steel and wood |
| EMULTEX™ FR 797 | VA Copolymer | 13 | 2 | 55% | 4.5 | Water-based | Waterborne intumescent fire protective coatings; fire resistance R90-120 min; low expansion ratio; protection for steel and wood |